Studies were carried out on the separation of the water-oil emulsion by polyamide membranes with a pore size of 0.2 μm treated with corona discharge plasma at a voltage of 5–25 kV and a time of 1–5 minutes. An increase in the productivity and efficiency of the separation of the water-oil emulsion by corona-treated polyamide membranes was revealed. Increase of roughness and change of chemical structure of modified membranes are shown.

全文:

受限制的访问

作者简介

V. Dryakhlov

Kazan National Research Technological University

编辑信件的主要联系方式.
Email: vladisloved@mail.ru
俄罗斯联邦, Kazan, Karl Marx St., 68

I. Shaikhiev

Kazan National Research Technological University

Email: vladisloved@mail.ru
俄罗斯联邦, Kazan, Karl Marx St., 68

D. Fazullin

Kazan (Volga Region) Federal University

Email: vladisloved@mail.ru

Naberezhnye Chelny Institute

俄罗斯联邦, Naberezhnye Chelny, ave. Mira, 68/19

I. Nizameev

Kazan National Research Technical University named after A.N. Tupolev

Email: vladisloved@mail.ru
俄罗斯联邦, Kazan, Karl Marx St., 10

M. Galikhanov

Institute of Applied Research, Tatarstan Academy of Sciences

Email: vladisloved@mail.ru
俄罗斯联邦, Kazan, Bauman str., 20

I. Mukhamadiev

Kazan National Research Technological University

Email: vladisloved@mail.ru
俄罗斯联邦, Kazan, Karl Marx St., 68

参考

  1. McCay D.F., Rowe J.J., Whittier N., Sankaranarayanan S., Etkin D.S. // J. Hazardous Materials. 2004. V. 107. P. 11.
  2. Pak A., Mohammadi T. // Desalination. 2008. V. 222. P. 249.
  3. Nassar N.N., Hassan A., Carbognani L., Lopez- F., Pereira-Almao P. // Fuel. 2012. V. 95. P. 257.
  4. Haruna A., Merican Z.M.A., Musa S.G. // J. Industrial and Engineering Chemistry. 2022. V. 112. P. 20.
  5. Deng S., Wang Z., Gu Q., Meng F., Li J., Wang H. // Fuel Processing Technology. 2011. V. 92(5). P. 1062.
  6. Peng B., Yao Z., Wang X., Crombeen M., Sweeney D.G., Tam K.C. // Green Energy & Environment. 2020 V. 5(1). P. 37.
  7. Albatrni H., Qiblawey H., Almomani F., Adham S., Khraisheh M. // Chemosphere. 2019. V. 233. P. 809.
  8. Varjani S., Joshi R., Srivastava V.K., Ngo H.H., Guo W. // Environmental Science and Pollution Research. 2020. V. 27. P. 27172.
  9. Mohammadi L., Rahdar A., Bazrafshan E., Dahmardeh H., Susan M.A.B.H., Kyzas G.Z. // Processes. 2020. V. 8(4). № 447.
  10. Dmitrieva E.S., Anokhina T.S., Novitsky E.G., Volkov V.V., Borisov I.L., Volkov A.V. // Polymers. 2022. V. 14(5). № 980.
  11. Muthukumar K., Kaleekkal N.J., Lakshmi D.S., et all. // J. Appl. Polym. Sci. 2019. № 24. P. 1–10.
  12. Fazullin D.D., Mavrin G.V. // Chemical and Petroleum Engineering. 2020. № 56. P. 215222.
  13. Шайхиев И.Г., Галиханов М.Ф., Дряхлов В.О., Алексеева М.Ю., Фазуллин Д.Д. // Вода: Химия и Экология. 2019. № 1–2 (118). С. 77–82.
  14. Алексеева М.Ю., Дряхлов В.О., Галиханов М.Ф., Низамеев И.Р., Шайхиев И.Г. // Мембраны И Мембранные Технологии. 2018. Т. 8. № 1. С. 59–65.
  15. Fedotova A.V., Shaikhiev I.G., Dryakhlov V.O., Nizameev. I.R., Abdullin I.S. // Petroleum Chemistry. 2017. V. 57. P. 159.
  16. Fedotova A.V., Dryakhlov V.O., Shaikhiev I.G., Nizameev I.R., Garaeva G.F. // Surface Engineering and Applied Electrochemistry. 2018. V. 54. P. 174.
  17. Shaikhiev I.G., Dryakhlov V.O., Galikhanov M.F., Fazullin D.D., Mavrin G.V // Inorganic Materials: Applied Research. 2020. V. 11. № 5. P. 1160–1164.
  18. Тарасов А.В., Федотов Ю.А., Лепешин С.А., Панов Ю.Т., Окулов К.В., Вдовина А.И. // Известия Самарского научного центра РАН. 2012. № 14 (1–9). С. 2372.
  19. Панов Ю.Т., Тарасов А.В., Лепешин С.А., Ермолаева Е.В. // Современные наукоемкие технологии. 2015. № 12–2. С. 258.
  20. Tusek L., Nitschke M., Werner C. //Colloids and Surfaces. A: Physicochemical and Engineering Aspects. 2001. V. 195. P. 81–95.
  21. Yang Z., Guo H., Tang Y.C. // Journal of membrane science. 2019. V. 590. P. 117297.
  22. Ridgway H.F., Orbell J., Gray S. // J. Membrane Science. 2017. V. 524. P. 436.
  23. Shao S., Zeng F., Long L., Zhu X., Peng L.E., Wang F., Yang Z. Tang C.Y. // Environmental Science & Technology. 2022. V. 56(18). P. 12811.

补充文件

附件文件
动作
1. JATS XML
下载
2. Fig. 1. Corona device diagram: 1 – high voltage source, 2 – grounded electrode, 3 – corona electrode, 4 – membrane sample.

下载 (45KB)
索引源数据
3. Fig. 2. Performance of separation of oil emulsion by PA membranes treated with corona discharge at: a) U = 5 kV; b) U = 15 kV; c) U = 25 kV.

下载 (269KB)
索引源数据
4. Fig. 3. Graph of the dependence of particle sizes and VNE intensity before and after corona treatment.

下载 (77KB)
索引源数据
5. Fig. 4. Diffraction pattern of the original and treated PA membrane with a pore size of 0.2 µm.

下载 (76KB)
索引源数据
6. Fig. 5. IR spectrum of the original and corona-treated PA membranes with a pore size of 0.2 µm.

下载 (79KB)
索引源数据
7. Fig. 6. Images of the surface with corresponding topographic histograms of the PA membrane: a) original; b) corona-treated.

下载 (878KB)
索引源数据

版权所有 © Russian Academy of Sciences, 2024