Layered Double Zinc and Aluminum Hydroxide Intercalated with Hexacyanoferrate(II) Ions for Extraction of U(VI) from Liquid Media

N. P. Ivanov; Иванов Н. П.; A. N. Drankov; Драньков А. Н.; E. K. Papynov; Папынов Е. К.; A. O. Lembikov; Лембиков А. О.; V. Yu. Mayorov; Майоров В. Ю.; A. N. Fedorets; Федорец А. Н.; G. D. Kaspruk; Каспрук Г. Д.

doi:10.31857/S004418562370064X

Layered Double Zinc and Aluminum Hydroxide Intercalated with Hexacyanoferrate(II) Ions for Extraction of U(VI) from Liquid Media

作者: Ivanov N.P.¹, Drankov A.N.¹, Papynov E.K.¹, Lembikov A.O.¹, Mayorov V.Y.¹, Fedorets A.N.¹, Kaspruk G.D.¹
隶属关系:
1. Far Eastern Federal University
期: 卷 59, 编号 5 (2023)
页面: 530-538
栏目: ФИЗИКО-ХИМИЧЕСКИЕ ПРОЦЕССЫ НА МЕЖФАЗНЫХ ГРАНИЦАХ
URL: https://vestnikugrasu.org/0044-1856/article/view/663945
DOI: https://doi.org/10.31857/S004418562370064X
EDN: https://elibrary.ru/VEMIXH
ID: 663945

如何引用文章

全文:

开放存取

##reader.subscriptionAccessGranted##
受限制的访问

订阅存取

详细
作者简介
参考
补充文件
统计

详细

Layered double zinc and aluminum hydroxide modified with hexacyanoferrate(II) ions was synthesized for the first time by reverse deposition. The obtained samples were studied by X-ray phase analysis, scanning electron microscopy, and low-temperature nitrogen adsorption, and their sorption characteristics with respect to uranium U(VI) were studied. The sorption capacity for the modified material under static conditions, determined by the Langmuir equation, was qmax
l = 156.70 ± 12.38 mg/g (at phase ratio V/m = 1000 mL/g, in a monocomponent solution of uranyl nitrate UO2(NO3)2 at a temperature T = 25°C and sorption time t = 24 h). Layered double zinc and aluminum hydroxide modified with hexacyanoferrate(II) ions is a promising sorbent for purification of liquid media from uranium U(VI) due to its high capacity and specific surface area, the possibility of effective use in a wide range of pH [4, 10], and low cost.

关键词

uranium(VI), layered double hydroxide, sorption

参考

Mittal J. // J. Environ. Manage. 2021. V. 295. P. 113017.
Faisal A.A.H., Shihab A.H., Naushad M. et al. // J. Environ. Chem. Eng. 2021. V. 9. № 4. P. 105342.
Farghali M.A., Selim A.M., Khater H.F. et al. // Arab. J. Chem. 2022. V. 15. № 11. P. 104171.
Mohiuddin I., Grover A., Aulakh J.S. et al. // J. Hazard. Mater. 2021. V. 401. P. 123782.
Barabi A., Seidi S., Rouhollahi A. et al. // Anal. Chim. Acta. 2020. V. 1131. P. 90.
Kim J., Kang J., Um W. // J. Environ. Chem. Eng. 2022. V. 10. № 3.
Mayordomo N., Rodríguez D.M., Rossberg A. et al. // Chem. Eng. J. 2021. V. 408. P. 127265.
Theiss F.L., Ayoko G.A., Frost R.L. // Chem. Eng. J. 2016. V. 395. P. 300.
Celik A., Baker D.R., Arslan Z. et al. // Chem. Eng. J. 2021. V. 426. P. 131696.
Behbahani E.S., Dashtian K., Ghaedi M. // J. Hazard. Mater. 2021. V. 410. P. 124560.
Papynov E.K., Tkachenko I.A., Majorov V.Y. et al. // Radiochemistry. 2019. V. 61. № 1. P. 28.
Kulyukhin S.A., Krasavina E.P. // Radiochemistry. 2016. V. 58. № 4. P. 405.
Kulyukhin S.A., Krasavina E.P., Rumer I.A. // Radiochemistry. 2015. V. 57. № 1. P. 69.
Dran’kov A.N., Balybina V.A., Buravlev I.Y. et al. // Russ. J. Inorg. Chem. 2022. V. 67. № 9. P. 1478.
Kulyukhin S.A., Krasavina E.P. // Radiochemistry. 2016. V. 58. № 4. P. 405.
Kong F., Xie Y., Xia C. et al. // Surf. Interfaces. 2023. V. 36. P. 102487.
Wu S., Liang H., Zhang Z. et al. // Opt. Mater. 2022. V. 131. P. 112636.
Chen S., Yang X., Wang Z. J. // J. Hazard. Mater. 2021. V. 410. P. 124608.
Shichalin O.O., Papynov E.K., Maiorov V.Y. et al. // Radiochemistry. 2019. V. 61. № 2. P. 185.
Dran’kov A., Shichalin O., Papynov E. et al. // Nucl. Eng. Technol. 2022. V. 54. P. 1991.
Bouali A.C., Iuzviuk M.H., Serdechnova M. et al. // Appl. Surf. Sci. 2019. V. 501. P. 144027.
Nagaraju Y.S., Ganesh H., Veeresha S. et al. // J. Energy Storage. 2022. V. 56. P. 105924.
Nakate U.T., Yu Y.T., Park S. // Ceram. Int. 2022. V. 48. P. 28822–28829.
Lyu P., Wang G., Wang B. et al. // Appl. Clay Sci. 2021. V. 209. P. 106146.
Guo Y., Gong Z., Li X. et al. // Chem. Eng. J. 2020. V. 392. P. 123682.